Irradiation-induced impurity segregation to grain boundaries is one of the important radiation effects on materials. For this reason, phosphorus segregation to prior austenite grain boundaries in a P-doped 2.25Cr1Mo steel subjected to neutron irradiation is examined using field emission gun scanning transmission electron microscopy (FEGSTEM) with energy dispersive X-ray microanalysis (EDX). The steel samples are irradiated around 270 and 400℃, respectively. The irradiation dose rate and dose are ～1.05×10-8 dpa/s and ～0.042 dpa respectively for 270℃ irradiation, and 1.7×10－8 dpa/s and 0.13 dpa respectively for 400℃ irradiation. The FEGSTEM results indicate that there is no apparent phosphorus segregation during 270℃ irradiation but there is some during 400℃ irradiation
关键词:
Neutron irradiation
,
null
,
null
,
null
Shenhua SONG
,
Luqian WENG
材料科学技术（英）
Quenching-induced phosphorus segregation to prior austenite grain boundaries in a 0.077 wt pct P-doped 2.25Cr-1Mo steel is examined using field emission gun scanning transmission electron microscopy (FEGSTEM). A phosphorus level of around 1.56 at. pct is observed for the water-quenched sample. In recognition of insufficiently high spatial resolution of the technique for grain boundary composition analysis, the measured results are corrected by an analytical convolution method. The corrected phosphorus segregation level may be up to about 4.7 at. pct. The quenching-induced phosphorus segregation is nonequilibrium segregation and the migration of vacancy-phosphorus complexes plays an important role in the kinetic process. For such a reason, the mechanism for migration of the complexes is discussed in some detail.
关键词:
Grain boundary
,
null
,
null
,
null